Small glass electrode

ABSTRACT

A small glass electrode and process for preparation thereof are disclosed. This small glass electrode is characterized in that said glass electrode, which has a bonded structure comprises a reference electrode composed of silver/silver chloride, a glass substrate having a pad embedded therein, said pad being composed of gold or platinum and circuit-connected to the reference electrode, and a silicon substrate having a (100) plane selectively etched by the anisotropic etching technique and comprising a groove for injecting an electrolyte composed of an aqueous solution containing chlorine such as KCl, or HCl, at least one hole for holding the electrolyte and a glass film formed in a portion corresponding to the reference electrode. By this structure, the small glass electrode can be easily manufactured at a low cost.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a small glass electrode and a process for the preparation thereof. More particularly, the present invention relates to a small glass electrode formed by utilizing a micro-machining technique and a process for the preparation thereof.

2. Description of the Related Art

A glass electrode is easily usable as a sensor for determining the hydrogen ion (H⁺) concentration in an aqueous solution, and is widely and generally used.

The determination of the H⁺ concentration is required not only in ordinary chemical experiments but also in fermentation control and in the medical field.

Furthermore, a biosensor fabricated by combining a glass electrode with either enzymes or microorganisms can be used for determining various chemical compounds.

For example, glucose reacts with dissolved oxygen with the aid of a catalyst called glucose oxidase and is oxidized to gluconolactone. Changes of the H⁺ concentration during this reaction are measured, and the glucose concentration can be determined from the changed quantities. According to a similar principle, the urea concentration can be determined.

In the glass electrode, the H⁺ concentration is measured by utilizing the electroconductivity of glass. Namely, the phenomenon that when a glass film having a thickness of about 100 μm and an electrical resistance of several hundred MΩ is placed in a solution, a voltage difference is produced according to the pH value of the solution which is utilized.

FIG. 1 illustrates the structure of a sensing portion of a conventional glass electrode, which comprises a reference electrode 2 composed of silver or silver/silver chloride (Ag/AgCl), an internal solution 4 such as a potassium chloride (KCl) solution having a certain concentration, and a spherical sensing glass film 6 formed on the top end.

When this glass electrode is immersed in a solution containing H⁺, in response to the active quantity (ai) of H⁺, a potential is generated according to the Nernst equation:

    E=const+(RT/F)lnai                                         (1)

wherein E represents the potential of the glass electrode, R represents the gas constant, T represents the absolute temperature, and F is the Faraday constant.

Accordingly, the H⁺ concentration is determined by the above equation.

However, the commercially available glass electrode has a size similar to that of a fountain pen, as shown in FIG. 1, and the glass electrode is formed by glazing and it is expensive.

An ion-sensitive electric field effect transistor (abbreviated to "ISFET") has been developed as a small H⁺ concentration sensor. Since a photolithographic technique of semiconductor production is utilized for its formation, the size thereof can be reduced.

In a device immersed in an aqueous solution, such as ISFET, insulation of the substrate is important.

Accordingly, many elements formed on a silicon (Si) substrate are diced into chips and a silicon nitride (Si₃ N₄) film is formed on the peripheries of the chips to effect insulation, or an SOS (silicon-on-sapphire) substrate is used. Alternatively, there is adopted a method in which a thin film transistor (TFT) is formed on a glass substrate. However, of the increased price of such a structure cannot be avoided and therefore, the sensor cannot be manufactured at a low price.

The conventional glass electrode formed by glazing is large size and expensive. In an ISFET formed by the photolithography of an Si substrate, insulation is indispensable and a price increase is inevitably caused by the necessity of maintaining the insulation, and reduction of the price is not easy.

Under this background, development of another method of providing a practical glass electrode of small size and low price is desired.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a small glass electrode capable of overcoming the foregoing problems and a process for the preparation thereof.

In accordance with one aspect of the present invention, this object can be attained by a small glass electrode, which has a bonded structure comprising a reference electrode composed of silver or silver/silver chloride, a glass substrate having a pad embedded therein, said pad being composed of gold or platinum and which is circuit-connected to the reference electrode, and a silicon substrate having a (100) plane selectively etched by the anisotroic etching technique and comprising a groove for injecting an electrolyte containing chlorine such as a potassium chloride buffer solution or hydrochloric acid solution, at least one reservoir for holding the electrolyte and a glass film formed in a portion corresponding to the reference electrode.

The glass film may have a multiple-layer (for example, two-layer) structure.

In accordance with another aspect of the present invention, there is provided a process for the preparation of a small glass electrode, which comprises selectively etching a glass substrate, forming a reference electrode, composed of silver or silver/silver chloride and a pad composed of gold or platinum and circuit-connected to the reference electrode, on the etched portion, subjecting a silicon substrate having a (100) plane as the substrate face to anisotropic etching to form an electrolyte-injecting groove and at least one electrolyte-holding reservoir therein, forming a glass film acting as a sensing film by utilizing a silicon oxide film as a mask, and bonding the formed glass substrate and silicon substrate to each other.

In accordance with still another aspect of the present invention, there is provided a process for the preparation of a small glass electrode, which comprises selectively etching a glass substrate, forming a reference electrode, composed of silver or silver/silver chloride and a pad composed of gold or platinum and circuit-connected to the reference electrode, on the etched portion, subjecting a silicon substrate having a (100) plane as the substrate face to anisotropic etching to form an electrolyte-injecting groove and at least one electrolyte-holding reservoir therein, removing the silicon oxide film which remains on the silicon substrate face, forming a glass film acting as a sensing film in a lower portion of the reservoir, and bonding the formed glass substrate and silicon substrate to each other.

The process of the present invention may further comprise a step of injecting the electrolyte into the reservoir from the injecting groove, according to need. Accordingly, a small glass electrode having an electrolyte injected in the reservoir is included within the scope of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

Objects as well as advantages of the present invention will be come clear from the following description of the preferred embodiments made with reference to the accompanying drawings; wherein:

FIG. 1 is a cross sectional view of a conventional glass electrode;

FIG. 2(A) is a planar view of a glass substrate in the glass electrode according to one embodiment of the present invention, FIG. 2(B) is a planar view of an Si substrate of the glass electrode according to this embodiment, and FIG. 2(C) is a planar view of the glass electrode of this embodiment of the present invention, formed by bonding the glass substrate and Si substrate shown in FIGS. 2(A) and 2(B);

FIG. 3(A) is a cross sectional view taken along line X--X' in FIG. (2) and FIG. 3(B) is a corresponding cross sectional view showing a modification of the glass electrode according to one embodiment of the present invention;

FIGS. 4(A) to 4(F) are diagrams illustrating steps of forming the glass electrode according to one embodiment of the present invention;

FIG. 5(A) is a planar view of a glass substrate in the glass electrode according to another embodiment of the present invention, FIG. 5(B) is a planar view of an Si substrate of the glass electrode according to this embodiment, and FIG. 5(C) is a planar view of the glass electrode of this embodiment of the present invention, formed by bonding the glass substrate and Si substrate shown respectively in FIGS. 5(A) and 5(B);

FIG. 6 is a cross-sectional view taken along line X--X' in FIG. 5(C);

FIGS. 7(A) to 7(F) are diagrams illustrating steps of forming the glass electrode according to another embodiment of the present invention;

FIG. 8(A) is a planar view of a glass substrate in the glass electrode according to still another embodiment of the present invention, FIG. 8(B) is a planar view of an Si substrate of the glass electrode according to this embodiment, and FIG. 8(C) is a planar view of the glass electrode of this embodiment of the present invention, formed by bonding the glass substrate and Si substrate shown respectively in FIGS. 8(A) and 8(B);

FIG. 9 is a cross-sectional view taken along line X--X' in FIG. 8(C);

FIGS. 10(A) to 10(F) are diagrams illustrating steps of forming the glass electrode according to still another embodiment of the present invention;

FIG. 11 is a diagram illustrating a response curve of the glass electrode of the present invention; and

FIG. 12 is a curve illustrating the relation between the change of the H⁺ concentration and the change of the electrode potential in the glass electrode of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present inventors already succeeded in providing a practical, utilizable small Clark oxygen electrode by applying the micro-machining technique to an Si substrate (U.S. Pat. No. 4,975,175).

This small oxygen electrode is often used for medical treatment. In this case, the oxygen concentration is measured relative to the H⁺ concentration, rather than the oxygen concentration alone.

Accordingly, practical utilization of a small glass electrode by using the micro-machining technique was tried.

The following plan describes said utilization by the present inventors:

(1) The size of the glass electrode, presently used as the H⁺ concentration sensor and found to operate well, is reduced.

(2) At least one holding hole (i.e., cavity or a reservoir) formed by anisotropic etching of an Si substrate, is used as a vessel for storing an electrolyte.

(3) A glass film formed by heat oxidation or sputtering is used as a sensing film (sensing element) for responding to the H⁺ concentration.

(4) A reference electrode is formed on a glass substrate, and the glass substrate and Si substrate are bonded and integrated by the anodic bonding method.

(5) A reference electrode composed of Ag/AgCl, a lead-in line and a pad are embedded in the glass substrate.

The glass substrate to be bonded to the Si substrate is required to adhere tightly to the Si substrate not only during the course of cooling from the anode bonding treatment temperature, of, about 250° C., to normal (i.e., ambient) temperature but also in the application atmosphere. For this purpose, it is required that (1) the glass substrate should have a thermal expansion coefficient approximately equal to that of Si, (2) the glass substrate should be composed of a glass material having a low softening point, and (3) the glass substrate should have a high resistance to thermal stress. In view of the foregoing, a heat resistant glass or lead glass such as Pyrex is preferably used. This glass alone can be used as the substrate, or this glass can be used in a state bonded to other glass substrates or an Si substrate.

Under this background, a glass electrode is formed by using the micro-machining technique according to the present invention.

In the glass electrode of the present invention, a thin glass film acting as the sensing film is formed by utilizing at least a part of an SiO₂ film obtained by wet oxidation of a wafer.

However, when a glass film having an increased strength is desired, the above-mentioned embodiment of the process for preparing a glass electrode is adopted in the present invention.

The thickness of the SiO₂ film formed by the wet oxidation of the silicon wafer is of about 1 μm in thickness, at the greatest, and it is impossible to increase the film thickness. Accordingly, in the process of the above-mentioned embodiment, a glass substrate is etched in advance to form a glass film having a desired thickness, a silicon oxide film remaining on the surface of the silicon substrate is removed, and then, the glass film is bonded to the bottom portion of the holding hole (i.e., cavity or reservoir).

In the so-prepared glass electrode of the second embodiment of the present invention, the strength of the glass film acting as the sensing film is increased. Therefore, the yield is improved and the glass electrode can be used without breaking.

In the respective glass electrodes obtained according to the above-mentioned two embodiments of the present invention, the sensitivity to the H⁺ concentration is in practice sufficiently high. However, when a glass electrode having a further enhanced sensitivity is desired, a glass electrode having a structure described below can be adopted.

The voltage generated at the glass electrode is generally represented by the following Nernst equation:

    E=constant-0.059 pH                                        (1)

However, this equation is a theoretical formula, and it is not easy to construct the glass electrode so that the potential in accordance with this equation is obtained.

When a sensing film is formed by using a heat resistant glass such as Pyrex having a thickness of about 50 μm, the gradient coefficient -0.059 (-59 mV) of the Nernst equation is about -0.03 (-30 mV).

Therefore, the present invention improves the glass material.

Lithium (Li) glass, sodium-calcium (Na--Ca) glass and the like are known as suitable glass materials for a glass electrode. However, in view of the heat resistance and strength limitations thereof, these materials cannot be used as the sensing film for a small glass electrode. The reasons are as follows.

(1) A heat treatment at about 800° C. is necessary for bonding to the Si substrate, for which the heat resistance is insufficient.

(2) A considerable strain is left after heat bonding, which these glass materials cannot/resist.

According to the present invention, a double-layer film, used as the sensing film, is obtained by forming a film of a glass material having excellent characteristics, such as a lithium glass or a sodium-calcium glass, by sputtering or vacuum deposition thereof on a film of a glass material which is insufficient as to the characteristics required for the sensing film, such as a Pyrex glass, whereby a glass electrode satisfying substantially, the requirement of the Nernst equation can be obtained.

In the present invention, it is sufficient if at least one holding hole is formed. However, if a plurality of holding holes are formed and glass films are bonded thereto, the risk of breaking the glass film is effectively reduced.

In the process of the present invention, bonding of the glass substrate and the silicon substrate is accomplished, for example, by a method of heating and bonding both substrates, a method using an adhesive or an anodic bonding method. From a practical viewpoint, the anode bonding method is preferably adopted.

The present invention will now be described in detail with reference to the following examples that by no means limit the scope of the invention.

EXAMPLE 1

FIG. 2(A) is a planar view of a glass substrate 10 of the glass electrode according to one embodiment of the present invention, FIG. 2(B) is a planar view of an Si substrate 20 of the glass electrode according to this embodiment, and FIG. 2(C) is a planar view of the glass electrode of this embodiment of the present invention, formed by inverting and assembling the glass substrate onto the Si substrate 20 and bonding them.

A reference electrode 12 composed of silver or Ag/AgCl, a lead-in line 14 composed of Au and a pad 16 composed of Au are embedded in the glass substrate 10.

The substrate face of the Si substrate 20 is the (100) plane, and the Si substrate 20 is subjected to anisotropic etching, whereby a groove 22 for injecting an electrolyte, an electrolyte-holding hole (i.e., a cavity or recess) 24 and a glass film 26 acting as the sensing film on at least a part of the hole 24 are formed. Incidentally, the groove only can also be made by the separate anisotropic etching.

In FIG. 2(C), the broken line indicates an interior glass electrode-forming region, and the pad 16 and glass film 26 appear on the side of the Si substrate 20.

FIG. 3(A) is a view showing the section taken along X--X' in FIG. 2(C). As is seen from FIG. 2(C) and FIG. 3(A), the sensing film 26 is formed adjacent the bottom portion of the cavity, or reservoir, of the etched Si substrate 20.

FIG. 3(B) is a sectional view showing a modification of this Example 1, where the Si substrate is etched also from the bottom so that the sensing film 26 is formed slightly on the inner side (i.e., on a recessed interior surface) of the Si substrate.

FIG. 4 is a diagram illustrating the steps of preparing the glass electrode of the present invention. One embodiment of the preparation process will now be described with reference to FIGS. 2(A)-2(C) and FIGS. 4(A)-4(F).

Formation of Glass Substrate:

A negative photoresist is spin-coated on the surface of a Pyrex glass substrate (Iwaki 7740) having a diameter of 2 inches and a thickness of 500 μm and is heated and dried at 150° C. for 30 minutes. Regions for formation of many reference electrodes 12, lead-in lines 14 and pads 16 are defined by corresponding windows in the photoresist and exposed by photolithography, and the same resist is similarly coated and dried on the back surface.

Then, the glass substrate is immersed in a mixed solution comprising 50% hydrofluoric acid (HF), concentrated nitric acid (HNO₃) and ammonium fluoride [(NH₄)F] at a ratio of 1/1/8 for 80 minutes to etch the glass substrate to a depth of 3 μm. Then, the resist is peeled off by using a mixed solution comprising sulfuric acid (H₂ SO₄) and hydrogen peroxide (H₂ O₂) at a ratio of 2/1 [see FIG. 4(A)].

Then, the glass substrate 10 is sufficiently washed with a mixed solution of H₂ O₂ and ammonia (NH₄ OH) and pure water, and is then dried.

Then, an Au film is vacuum-deposited on the glass substrate 10. Since Au adheres very poorly to glass, a very thin chromium (Cr) film is vacuum-deposited on the glass substrate in advance to improve the adhesiveness.

The thickness of the Cr film is 400 Å and the thickness of the Au film is 4000 Å.

Then, a positive resist film (DFRP-5000 supplied by Tokyo Oka) is spin-coated, and the resist is coated on regions for forming reference electrodes 12, lead-in lines 14 and pads 16 by the photolithography. Then, the Au film and Cr film are selectively etched to form a reference electrode pattern comprising reference electrodes 12, lead-in lines 14 and pads 16.

The Au-etching solution is formed by dissolving 4 g of KI and 1 g of I₂ in 40 ml of water, and the Cr-etching solution is formed by dissolving 0.5 g of NaOH and 1 g of K₃ Fe(CN)₆ in 4 ml of water.

Then, silver (Ag) is vacuum-deposited on the portion for forming the reference electrode 12, and in the same manner as described above, coating of a positive resist, heat-drying, light exposure and development are carried out to coat the resist only on the reference electrode-forming portion. Then, Ag etching is conducted and the resist is dissolved and removed, whereby a silver film is formed on the reference electrode-forming portion.

The Ag-etching solution is one comprising 29% NH₄ OH, 31% H₂ O₂ and pure water at a ratio of 1/1/20.

Then, the entire substrate is sufficiently washed with pure water and immersed in a 0.1M solution of FeCl₃ for 10 minutes to form a thin AgCl layer on the surface of Ag.

Then, the entire substrate is sufficiently washed with pure water to complete reference electrodes 12, lead-in lines 14 and pads 16 [FIG. 4(B)].

Formation of Si Substrate:

An Si substrate 20 having a (100) plane as the substrate face and having a thickness of 350 μm and a diameter of 2 inches is prepared, sufficiently washed with a mixed solution of H₂ O₂ and NH₄ OH and pure water, and dried. The Si substrate 20 is subjected to wet oxidation at 1050° C. for 200 minutes to form an SiO₂ film 28 having a thickness of 1 μm on the entire surface.

A negative resist (OMR-83 supplied by Tokyo Oka) having a viscosity of 60 cP is coated on the surface of the Si substrate, and light exposure, development and rinsing are carried out to form a resist pattern on the substrate. Then, the Si substrate 20 is immersed in a mixed solution comprising 50% HF and 40% NH₄ F at a ratio of 1/6 and the exposed portion of SiO₂ is etched and removed to form a holding hole 24 [see FIG. 4(C)].

Then, the resist film is peeled off in a mixed solution comprising sulfuric acid and hydrogen peroxide at a ratio of 2/1. Then, the Si substrate 20 is immersed in 35% KOH at 80° C. and anisotropic etching of silicon is carried out to form the electrolyte-holding hole 24 in the reference electrode portion (FIG. 4(D)).

A glass film 26 acting as the sensing film is formed adjacent the bottom portion of the holding hole (reservoir) 24 by utilizing an SiO₂ film 28 having a thickness of 1 μm, formed by wet oxidation.

If the SiO₂ used as the mask is left on the surface of the Si substrate 20, a higher temperature is necessary for the anodic bonding. Therefore, SiO₂ other than the glass film 26 is completely removed by the photolithography using a mixed solution comprising 50%HF and 40% NH₄ F at a ratio of 1/6. Thus, a vessel portion for storing an electrolyte is completed [see FIG. 4(D)].

Bonding of Glass Substrate and Si Substrate:

The so-prepared glass substrate 10 and Si substrate 20 are immersed in pure water, sufficiently washed under ultrasonic vibrations and dried, and the substrates are bonded to each other by applying a voltage of 1200 V at a temperature of 250° C. across the substrates, with the Si substrate 20 located on the positive side and the glass substrate 10 located on the negative side, whereby the anodic bonding of the glass substrate and the silicon substrate is effected [see FIG. 4(E)].

Many glass electrode elements formed on the substrate are cut out into chips by using a dicing saw to obtain a small glass electrode.

When the so-obtained small glass electrode is used, an electrolyte is introduced into the interior of the electrode according to the following method.

A beaker is charged with 0.1M hydrochloric acid aqueous solution or an aqueous potassium chloride buffer solution contining a phosphoric acid (electrolyte), and the glass electrode is entirely immersed in the electrolyte and the entire system including the beaker is placed in a sealed vessel. Then, deaeration is carried out by a vacuum pump.

After bubbles have not come out of the groove 22 for injecting the electrolyte 30, air is introduced into the vessel. The hole can be filled with an epoxy regin.

By the above operation, the electrolyte is introduced into the inner space of the electrode, whereby a small glass electrode is obtained [see FIG. 4(F)].

According to this embodiment, a fine glass electrode can be prepared by using the micro-machining technique while maintaining a wafer-like shape. Accordingly, reduction of the device cost is possible.

Furthermore, since the glass electrode can be stored in a dry state, long-period storage is possible.

EXAMPLE 2

Another embodiment of the process for preparing the glass electrode of the present invention will now be described.

FIG. 5(A) is a planar view of a glass substrate of the glass electrode according to another embodiment of the present invention, FIG. 5(B) is a planar view of an Si substrate of the glass electrode according to this embodiment, and FIG. 5(C) is a planar view of the glass electrode of this embodiment of the present invention, formed by bonding the glass substrate and Si substrate respectively in FIGS. 5(A) and 5(B).

FIG. 6 is a cross-section taken along line X--X' in FIG. 5(C).

FIGS. 7(A) to 7(F) are diagrams illustrating steps of forming the glass electrode according to another embodiment of the present invention.

In FIGS. 5(A) through 7(F), the identical reference numerals represent the same members as in FIGS. 1 through 4 unless otherwise indicated.

The glass substrate-forming step is the same as described in Example 1. Accordingly, the description is omitted.

Furthermore, the Si substrate is prepared substantially in the same manner as described in Example 1, except that a part of the SiO₂ film is not utilized as the glass film acting as the sensing film, but the SiO₂ film is entirely removed.

Bonding of Glass Film to Si Substrate:

A heat resistant glass such as Pyrex (Iwaki 7740) is etched in a mixed solution comprising 50% HF and concentrated HNO₃ at a ratio of 2/1 to obtain a film having a thickness of about 50 μm, and the film is sufficiently washed to obtain a glass film 26 acting as the sensing film 26A.

The glass film 26A is placed on the surface of the Si substrate 20, which is previously processed formed by perforating the Si substrate by the anisotropic etching to include the reservoir 24, and heated at 800° C. to effect bonding [see FIG. 7(D)].

Bonding of the so-prepared glass substrate and Si substrate [FIG. 7(E)] and injection of the electrolyte [FIG. 7(F)] are carried out in the same manner as described in Example 1.

According to this embodiment of the present invention, the strength of the glass film of the formed glass electrode is increased and hence, the yield is increased, and the glass electrode is advantageous over the conventional glass electrode in that no breaking is caused during use.

EXAMPLE 3

Still another embodiment of the process for preparing the glass electrode of the present invention will now be described.

FIG. 8(A) is a planar view of a glass substrate of the glass electrode according to still another embodiment of the present invention, FIG. 8(B) is a planar view of an Si substrate of the glass electrode according to this embodiment, and FIG. 8(C) is a planar view of the assembled glass electrode of this embodiment of the present invention, formed by bonding the glass substrate respectively and Si substrate shown in FIGS. 8(A) and 8(B).

FIG. 9 is a cross section taken along line X--X' in FIG. 8(C).

FIGS. 10(A) to 10(F) are diagrams illustrating steps of forming the glass electrode according to this embodiment of the present invention.

In FIGS. 8 through 10, identical reference numerals represent the same members as in FIGS. 1 through 4 unless otherwise indicated.

The glass substrate-forming step is the same as described in Example 1. Accordingly, the description is omitted.

Furthermore, the Si substrate is prepared substantially in the same manner as described in Example 1, except that a part of the SiO₂ film is not utilized as the glass film acting as the sensing film, but the SiO₂ film is entirely removed.

Bonding of Glass Film to Si substrate:

A heat resistant glass such as Pyrex (Iwaki 7740) is etched in a mixed solution comprising 50% HF and concentrated HNO₃ at a ratio of 2/1 to obtain a film having a thickness of, for example, 20-150 μm, in this case 50 μm, and the film is sufficiently washed to obtain a first glass film 29A constituting a film 29A acting as the sensing film.

The first glass film 29A is placed on the back surface of an Si substrate 20 having a perforated or piercing holding hole (reservoir) 24 formed by anisotropic etching of an Si substrate and heated at 750° C. to effect bonding of the first glass film 29A to the Si substrate 20. Then, the Si substrate having the first glass film formed thereon is placed in a sputtering device and an sodium-calcium Na--Ca glass is sputtered in a thickness of 500 nm to form a second glass film 29B on the first glass film 29A, whereby a double-layer glass film 26B acting as the sensing film is obtained [see FIG. 10(D)].

Bonding of the so-prepared glass substrate and Si substrate [FIG. 10(E)] and injection of an electrolyte [FIG. 10(F)] are carried out in the same manner as described in Example 1, whereby a small glass electrode is obtained.

The characteristics of the small glass electrode obtained in Example 3 are evaluated according to the following method.

The evaluation is performed by monitoring changes of the potential of the glass electrode relative to the potential of an external reference electrode of silver/silver chloride by using an electrometer. For examining changes of the potential relative to changes of the pH value, the sensing portion of the electrode is immersed in a 10 mM TRIS (Trimethyl aminomethane) solution, and HCl is added to reduce the pH value. At each pH value, the potential of the glass electrode is examined. The experiment is conducted at 25° C.

The response curve obtained when the pH value of the external buffer solution is changed is shown in FIG. 11.

As is seen from FIG. 11, a very clear response curve is obtained. When the pH value is changed, the small glass electrode immediately shows a change and a 90% response time is 10 seconds. A change of the electrode potential observed when the pH value is changed is shown in FIG. 12. It is seen that a linear relation is established between them over a broad pH value range of from 2 to 10. The gradient of the linear relation is a value approximate to -59 mV/pH of the theoretical value of the Nernst equation at 25° C. 

I claim:
 1. A small glass electrode having a bonded structure and comprising: a reference electrode composed of silver/silver chloride, a glass substrate having a pad embedded therein, said pad being composed of gold or platinum and circuit-connected to the reference electrode, and a silicon substrate having a first main surface defined by a (100) plane and which is selectively etched by anisotropic etching to define a reservoir for holding an aqueous electrolyte, the reservoir extending from the first main surface and to a second, opposite main surface and having a sidewall at the second main surface of the silicon substrate, and a groove in communication with the reservoir for injecting the aqueous electrolyte into the reservoir, and a glass film formed on said silicon substrate at the second main surface thereof in a portion of the sidewall of the reservoir at a position corresponding to that of the reference electrode.
 2. A small glass electrode as set forth in claim 1, wherein an electrolyte occupies the electrolyte-holding reservoir.
 3. A small glass electrode as set forth in claim 1, wherein the glass film is a sensing film and comprises two layers of glass film.
 4. A small glass electrode having a bonded structure comprising:a glass substrate having a first main surface and having embedded therein, from the main surface, a reference electrode, a pad and a lead-in line interconnecting said reference electrode and said pad; a silicon semiconductor substrate having a first main surface, at least one reservoir extending into the substrate from the first main surface for holding an aqueous electrolyte and a groove forming a fluid passageway in communication with the reservoir for injecting the aqueous electrolyte into the reservoir, said groove and said reservoir being formed by anisotropic etching of the substrate, the reservoir extending from the first main surface and toward a second, opposite main surface of the semiconductor substrate and the reservoir having a sidewall defining an aperture at the second main surface of the silicon substrate to expose the interior of the reservoir, the aperture being disposed at a location corresponding to the position of the reference electrode embedded in the glass substrate; and a glass sensing film covering and sealing the aperture in the sidewall and thus at a position corresponding to said reference electrode.
 5. A small glass electrode as set forth in claim 4, wherein said reference electrode is comprised of silver or silver/silver chloride.
 6. A small glass electrode as set forth in claim 4, wherein said pad and said lead-in line are made of gold or platinum.
 7. A small glass electrode as set forth in claim 4, wherein said electrolyte is an aqueous electrolyte solution.
 8. A small glass electrode as set forth in claim 4, wherein the glass film is a sensing film and comprises two layers of glass film.
 9. A small glass electrode as set forth in claim 4, wherein said semiconductor substrate is a (100) oriented silicon substrate.
 10. A small glass electrode as set forth in claim 4, wherein said glass film comprises two layers of glass film.
 11. A glass electrode structure comprising:a glass substrate comprising a first, end portion, a second, central portion and a third, end portion, the third end portion being opposite the first end portion and integrally connected thereto by the second central portion, the first, second and third portions having corresponding first, second and third main surface portions lying in a common plane and defining a common main surface of the glass substrate, the glass substrate having opposite end walls respectively associated with the first and second opposite end portions and a pair of spaced, lateral sidewalls respectively interconnecting the end walls, and the main surface including a peripheral main surface portion extending inwardly from each of the lateral sidewalls and the end walls of the glass substrate and defining an interior main surface portion; a conductor layer embedded in the interior main surface portion and comprising a reference electrode portion formed on the interior of the first main surface portion, an electrical conducting pad on the interior of the third main surface portion and an interconnecting lead formed on the interior of the second main surface portion and extending between and electrically interconnecting the pad and the reference electrode, the pad and the lead comprising a common material selected from the group consisting of gold and platinum material and the reference electrode comprising a layer of silver formed on the interior of the first main surface portion and a layer of silver chloride formed on the layer of silver; a silicon substrate having a first main surface defined by a (100) plane thereof and an opposite main surface, and further having a pair of spaced, opposite end walls and a pair of spaced, lateral sidewalls respectively extending between and interconnecting the opposite end walls, the silicon substrate further comprising a first, end portion and an integral, second portion having respective first and second main surface portions comprising the first main surface of the substrate and respectively corresponding to the first and second main surface portions of the glass substrate, the silicon substrate further having a peripheral main surface portion extending inwardly from each of the lateral sidewalls and the end walls thereof and defining an interior main surface portion, a recess in the first, end portion and a groove extending from the recess and along the first main surface of the silicon substrate to the second end wall thereof, the recess being bounded by the peripheral main surface portion and extending from the interior main surface portion to the opposite main surface of the substrate and defining an aperture at a position at least adjacent to the opposite main surface, the aperture being closed by a glass film; and the glass substrate and the silicon substrate being assembled with the respective main surfaces thereof in contiguous and aligned relationship with the first and second main surface portions of the silicon substrate disposed on the first and second main surface portions of the glass substrate and with the peripheral main surface portion of the silicon substrate bonded to the corresponding peripheral and main surface portions of the glass substrate and thereby with the reference electrode in registry with the recess and defining therewith a reservoir, the groove in the silicon substrate defining a fluid passageway, extending from the reservoir and between the glass and silicon substrates to the second end wall of the silicon substrate to and of sufficient depth for the injection of a liquid electrolyte solution therethrough into the reservoir.
 12. A small glass electrode as recited in claim 11, further comprising an electrolyte injected through the groove and received in the reservoir.
 13. A small glass electrode as recited in claim 12, wherein the glass and silicon substrates are bonded together by anodic bonding.
 14. A small glass electrode as recited in claim 11, wherein the aperture is defined at a recessed position within the silicon substrate, displaced inwardly of the second main surface thereof, and the glass film is positioned at the recessed position of the aperture and secured about the peripheral edges thereof to the corresponding edge walls of the aperture.
 15. A small glass electrode as recited in claim 14, wherein the glass film is secured to the silicon substrate by anodic bonding.
 16. A small glass electrode as recited in claim 11, wherein the glass film comprises a double layer glass film.
 17. A small glass electrode as recited in claim 16, wherein the double layer glass film comprises a first layer of a heat resistant glass and a second, sputtered layer of sodium-calcium glass.
 18. A small glass electrode as recited in claim 11, wherein each of the recess and the groove is formed by anisotropic etching of the silicon substrate, inwardly from the first main surface thereof.
 19. A small glass electrode as set forth in claim 11, wherein the glass film is a sensing film and comprises two layers of glass film. 